Fenómeno do problema
PU products crack under stress + chemicals in <100h
Análise das causas
PU molecular chains under stress are attacked accelerated by chemicals; environmental stress cracking is a typical failure mode of polyolefins
Solução
1) Reduce product internal stress by annealing; 2) Select high molecular weight PU to improve ESC resistance; 3) Avoid contact with aggressive chemicals
Conclusão principal
Stress cracking is caused by stress-accelerated chemical attack; annealing and high MW are key