Molding Process
5 views
Large EAA compression set
Problem Phenomenon
EAA product compression set >30% below the 15% requirement
Cause Analysis
EAA elastic recovery insufficient; crosslinking degree too low, plastic deformation unrecoverable; density too low, thin cell walls with poor recovery
Solution
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) Select high elastic recovery EAA grade; 3) Add reinforcing filler
Key Takeaway
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key