Molding Process
5 views
Coarse EEA internal crystallization
Problem Phenomenon
EEA products with internal spherulites >50μm, coarse, causing transparency decline and low impact
Cause Analysis
Cooling rate too slow <5°C/min allowing spherulites to fully grow; no nucleating agent used to control crystallization
Solution
1) Increase cooling rate to >20°C/min to refine spherulites; 2) Add 0.2-0.3wt% nucleating agent to control crystallization; 3) Reduce mold temperature to accelerate cooling
Key Takeaway
Coarse crystallization is caused by slow cooling; fast cooling and nucleating agent are key