Molding Process
5 views
POE compression set large
Problem Phenomenon
POE product compression set >30%, below 15% requirement
Cause Analysis
POE elastic recovery insufficient; crosslinking degree low, plastic deformation unrecoverable; density low, cell walls thin, recovery poor
Solution
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) Select high elastic recovery POE grade; 3) Add reinforcing filler
Key Takeaway
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key