Extrusion & Post
13 visualizações
Melt fracture in PVA extrusion
Fenómeno do problema
When extrusion rate is too high, PVA shows severe melt fracture, extrudate twisted in spiral shape
Análise das causas
PVA melt elasticity too high, elastic recovery at die exit exceeds critical value; die L/D ratio too short <10, melt not fully relaxed; extrusion temperature too low
Solução
1) Reduce extrusion rate to 2-3m/min; 2) Increase die length-to-diameter ratio to 15-20; 3) Increase extrusion temperature to 140-200°C; 4) Add a small amount of low-elasticity resin to reduce system elasticity; 5) Gradually converging die entrance design
Conclusão principal
Melt fracture is caused by elastic recovery exceeding the critical value; reducing speed and lengthening the die are the core countermeasures