Molding Process
5 views
DSTDP large compression set
Problem Phenomenon
DSTDP product compression set >30%, below the 15% requirement
Cause Analysis
DSTDP elastic recovery insufficient; crosslinking degree on the low side, plastic deformation unrecoverable; density on the low side, cell walls thin, poor recovery
Solution
1) Increase crosslinking degree to 60-70% to reduce plastic deformation; 2) select high elastic recovery DSTDP grades; 3) add reinforcing filler
Key Takeaway
Large compression set is caused by insufficient crosslinking; increasing crosslinking degree is key